Pemanfaatan Limbah Serat Kelapa Sebagai Bahan Pengisi List Profile
Sari
The potential for coconut wood industrial waste in Indonesia is enormous, producing sawdust, wood chips and sawdust by 40%. Coconut coir waste is a material containing lignocellulosic which can be used as an alternative raw material for making list profiles. The research aims to determine the type and level of adhesive on the list profile properties of coconut fiber waste. This study used a completely randomized design with Tukey's follow-up test. The factors used were the type of adhesive (gypsum, white cement and a mixture of gypsum and white cement) and the amount of adhesive (600 g, 690 g and 780 g). Parameters observed were density, water absorption, thickness expansion and elastic modulus. The results showed that the type and amount of adhesive had a significant effect on all the parameters studied. Density value is 0.67-0.92 g/cm3, water absorption is 18.31 - 33.87 %, thickness expansion is 0.36 - 2.54 % and elastic modulus is 1158.06 -11145.31 kg/cm2. Coconut fiber waste can be used as a filler for list profiles.
Keywords: List profile, gypsum, white cement, adhesive content
Teks Lengkap:
PDF 158-162Referensi
Abdurachman, Hadjib, N. dan Adi Santoso. 2014. Penerapan Teknologi Laminasi dalam Pembuatan Rumah Kayu. Prosiding Seminar Hasil Penelitian. Pusat Penelitian dan Pengembangan Hasil Hutan. Badan Penelitian Pengembangan dan Inovasi. Bogor.
Adi Santoso dan Gustan Pari. 2015. Sifat Papan Partikel Daur Ulang Rendah Emisi Formaldehida. Jurnal Penelitian Hasil Hutan Vol. 33 No. 1, Maret 2015: 1 – 10. ISSN: 0216-4329.
Aminah, Setyawati D, Yani A. 2018. Sifat Fisik dan Mekanik Papan Partikel dari Limbah Kayu Acacia Crassicarpa pada Beberapa Ukuran Partikel dan Konsentrasi Urea Formaldehida. Jurnal Hutan Lestari 6.(3) : 557 – 568.
Anonim.2018. Mengenal Potensi Limbah Kelapa Sawit Indonesia. https://kumparan. com/noviyanti-nurmala1519197736585/ dari-limbah-menjadi-berkah-mengenal-potensi-limbah-kelapa-sawit-indonesia. Diakses pada tanggal 17 Januari 2020.
Aprillia, M. Dirhamsyah, Yuliati Indrayani, 2019. Physical-Mechanical Properties of Particle Board from Veener Waste Based on Pressing Time and Urea Formaldehyde Concentration. Jurnal Hutan Lestari (2019) Vol. 7 (4) : 1549 – 1561.
Badan Standardisasi Nasional. 2006. Papan Partikel. Standard Nasional Indonesia (SNI 03-2105-2006). Jakarta: Badan Standardisasi Nasional.
Fernanda Dinhane, Isabela Imakawa de Araújo, Ivaldo de Domenico Valarelli, Cristiane Inácio de Campos. 2015. Particleboard Manufactured with Bamboo and Coconut Fibers in Different Ratios of Adhesive. https://www.researchgate. net/publication/276367950_Particleboard_Manufactured_with_Bamboo_and_Coconut_Fibers_in_Different_Ratios_of_Adhesive. Diakses pada
Hasan, Abu , Muhammad Yerizam, Mutmainnah Ningtyas Kusuma, 2020. Papan Partikel Ampas Tebu (Saccharum officinarum) Dengan Perekat High Density Polyethylene . Jurnal Kinetika ISSN: 1693-9050/ E-ISSN: 2623-1417. Vol. 11, No. 03 (November 2020) : 8-13.
Lee , Seng Hua, Wei Chen Lum , Jia Geng Boon , Lubos Kristak, Petar Antov , Marta Pe˛dzik , Tomasz Rogozinski , Hamid R. Taghiyari, Muhammad Adly Rahandi Lubis , Widya Fatriasari, Sumit Manohar Yadav, Aujchariya Chotikhun , Antonio Pizzi, 2022. Particleboard from agricultural biomass and recycled wood waste: a review https://doi.org/10.1016/ j.jmrt. 2022.08.166 2238-7854/© 2022 The Author(s). Published by Elsevier B.V. This is an open access article under the CC BY license (http://creative- commons.org/ licenses/by/4.0/).
Marsoem, Sri Nugroho, Joko Sulistyo dan J.P. Gentur Sutapa. 2012. Buku Ajar Sifat-sifat Dasar Kayu, Fakultas kehutanan UGM Yogyakarta.
Prawirohatmodjo, Soenardi. 2012. Sifat – Sifat Fisika Kayu. Pelajaran Yang Berharga Untuk Perbaikan Kualitas Produk. Penerbit Cakrawala.
Prayitno, T.A. 2012a. Teknologi Perekatan Kayu. Bagian Penerbitan Yayasan Pembina Fakultas Kehutanan UGM. Yogyakarta.
__________, 2012b. Pengaruh Perlakuan Panas Dengan Metode Kukus (Steam) Terhadap Sifat-Sifat Kayu Nangka Untuk Produk Perekatan Dan Finishing. Laboratorium Penggergajian Dan Papan Majemuk Bagian Teknologi Hasil Hutan Fakultas Kehutanan Universitas Gadjah Mada. November 2012.
Santoso, Mahdi, Desy Natalia Koroh, Prona Rogaya Rambe, Grace Siska, Yanarita1 2022. Sifat Fisika dan Mekanika Papan Partikel Berbahan Limbah Industri Kayu PT. Aldi Mandomai Mebel. Jurnal Hutan Tropika e-ISSN: 2656-9736 / p-ISSN: 1693-7643 Vol. 17 No. 1 / Juni 2022 Hal. 114-123.
Sudarsono, Toto Rusianto, Yogi suryadi, 2010. Pembuatan Papan Partikel Berbahan Baku Sabut Kelapa Dengan Bahan Pengikat Alami (Lem Kopal). Jurnal Teknologi, Volume 3 Nomor 1 , Juni 2010, 22-32.
Sushardi. 2001. Pemanfaatan Limbah Pertanian untuk Pembuatan Papan Tiruan. Proseding Seminar Nasional “Pemanfaatan Sumberdaya Lokal untuk Pembangunan Pertanian Berkelanjutan “ Universitas Wangsa Manggala, Yogyakarta. ISBN: 979-96792-0-6.
_______. 2003a. Variasi Ketahanan Beberapa Produk Perekatan terhadap Air. Prosiding Seminar Nasional Penerapan Teknologi Tepat Guna dalam Mendukung Agribisnis Tanggal 24 September 2003. ISBN 979-8073-88-6.
_______. 2003b. Pemanfaatan Limbah Industri Kayu untuk Pembuatan Papan Semen. Prosiding Semiloka Nasional Pembangunan Perkebunan dan Perhutanan dalam Era Otonomi Daerah Tanggal 8 - 9 Desember 2003. ISBN : 979-97725-2-4.
_______. 2010. Pemanfaatan Limbah Plastik Jenis Polypropylene Untuk Pembuatan Papan Komposit Limbah Serbuk Gergaji Sengon. Prosiding Seminar Nasional Pertanian Indonesia Menuju Mellenium Development Goals (MDGs) 2015. ISBN 978-979-25-5261-4
_______. 2011. Peningkatan Sifat Papan Partikel Limbah Kayu Kelapa Dengan Perlakuan Permukaan. Prosiding Seminar Nasional Masyarakat Peneliti Kayu Indonesia.
_______. 2015a. Kualitas Kayu Lapis dari Kombinasi Kayu Akasia dan Sungkai. Jurnal Hutan Tropika. Jurusan/Prodi Kehutanan Fakultas Pertanian Universitas Palangka Raya. Volume X No I Juni 2015. ISSN 1693-7643.
_______. 2015b. Pemanfaatan Limbah Plastik dan Serbuk Gergaji Sengon Untuk Pembuatan Papan Komposit. Prosiding Seminar Nasional The 2nd University Research Colloquium tanggal 29 Agustus 2015 Universitas Muhammadiyah Semarang. ISSN 2407-9189.
Sushardi dan Achmad Abdurrahim. 2015. Pemanfaatan Limbah Kayu Kelapa Untuk Pembuatan Papan Partikel. Seminar Nasional Hasil - Hasil Penelitian dan Pengabdian LPPM Universitas Muhammadiyah Purwokerto, Sabtu, 26 September 2015.
Sushardi dan Restu. 2017. Pemanfaatan Limbah Plastik dan Serbuk Gergaji Sengon Untuk Pembuatan Papan Komposit. Prosiding Seminar Nasional The 2nd University Research Colloquium tanggal 29 Agustus 2015 Universitas Muhammadiyah Semarang. ISSN 2407-9189.
Sushardi and M. N. A. Azman. 2020, “Utilization of wood industry waste as raw material for cement boards production,†Int. J. Adv. Sci. Technol., vol. 29, no. 4 Special Issue, pp. 1897–1902, 2020.
Sushardi, Ruswanto A, Gunawan S, et al 2020. The selection of environmentally friendly wood for raw materials in the creative industries. Syst Rev Pharm. 2020;11(11): 523-528. doi:10.31838/srp.2020.11.75
Sushardi, Hastanto BW, Siman Suwadji dan Didik Surya Hadi, 2022. Perbaikan Sifat List Profile Limbah Serat Kelapa Dengan Perlakuan Jenis dan Jumlah Perekat. Prosiding Universitas Islam Batik Surakarta 14 juli 2022. ISBN : 978-979-1230-74-2.
Tifani, E.,dan Indriyani Puluhulawa. 2018. Sifat Fisik dan Mekanis Papan Partikel dari Kulit Pinang dan Serbuk Kayu Mahang. Seminar Nasional Industri dan Teknologi (SNIT), Politeknik Negeri Bengkalis.
Refbacks
- Saat ini tidak ada refbacks.